- High flflexibility
- Good tear resistance
- Highly accurate
- Excellent white color
- Footwear
- Prototypes need rubber like material
- Soft white display models
| Appearance | White | Dp | 13.5 mJ/cm2 | [critical exposure] |
| Viscosity | 560 cps@30℃ | Ec | 0.125 mm | [slope of cure-depth vs. In (E) curve] |
| Density | 1.1 g/cm3 | Building layer thickness | 0.08-0.12 mm |
| Mechanical Properties | UV Postcure | |
| MEASUREMENT | TEST METHOD | VALUE |
| Hardness , Shore D | ASTM D 2240 | 72-78 |
| Flexural modulus , Mpa | ASTM D 790 | 2,680-2,775 |
| Flexural strength , Mpa | ASTM D 790 | 65- 75 |
| Tensile modulus , MPa | ASTM D 638 | 2,170-2,385 |
| Tensile strength , MPa | ASTM D 638 | 25-30 |
| Elongation at break | ASTM D 638 | 12 -20% |
| Impact strength, notched lzod, J/m | ASTM D 256 | 58 - 70 |
| Heat deflection temperature, ℃ | ASTM D 648 @66PSI | 50-60 |
| Glass transition, Tg | DMA，E”peak | 55-70 |
| Density , g/cm3 | 1.14-1.16 | |