Superior Comprehensive Properties Vacuum Casting PA like

PHYSICAL PROPERTIES
		PX 226PART A	PX 226 - PX 226/L PART B
Composition		ISOCYANATE	POLYOL	MIXED
Mix ratio by weight		100	50
Aspect		liquid	liquid	liquid
Color		Pale yellow	colorless	white
Viscosity at 77°F(25°C)       (mPa.s)	BROOKFIELD LVT	175	700	2,000(1)
Density at 77°F(25°C)Density of cured product at 73°F(23°C)	ISO 1675 : 1985ISO 2781 : 1996	1.22-	1.10-	1.20
Pot life at 77°F(25°C)on 500 g   (minutes) (Gel Timer TECAM)	PX 226  PART B PX 226/L PART B			47.5

Processing Conditions Heat both parts (isocyanate and polyol) at 73°F(23°C) in case of storage at low temperature. Important : Shake vigorously part A before each weighing. Weigh both parts. After degassing for 10 minutes under vacuum mix for 1 minute with PX 226-226 2 minutes with PX 226-226/L Cast under vacuum in a silicone mold, previously heated at 158°F(70°C). Demold after 25 - 60 minutes minimum at 158°F(70°C) (allow the part to cool down before demolding). Handling Precautions Normal health and safety precautions should be observed when handling these products : Ensure good ventilation Wear gloves, safety glasses and impervious clothing. For further information, please consult the material safety data sheet.

Flexural modulus of elasticity	ISO 178 :2001	Psi/(MPa)	363,000/(2,500)
Flexural strength	ISO 178 :2001	Psi/(MPa)	15,000/(105)
Tensile strength	ISO 527 :1993	Psi/(MPa)	10,000/(70)
Elongation at break in tension	ISO 527 :1993	%	15
Charpy impact strength	ISO 179/1eU :1994	Ft-lbf/in2/(kJ/m2)	33/(70)
Hardness	ISO 868 :2003	Shore D1	82

Glass transition temperature(2)	ISO 11359 : 2002	°F/(°C)	221/(105)
Heat deflection temperature(2)	ISO 75Ae :2004	°F/(°C)	198/(92)
Linear shrinkage(2)	-	%	0.3
Maximal casting thickness	-	In/(mm)	5
Demolding time at 158°F/(70°C)	PX 226  PART B PX 226/L PART B	minutes	25, 60

Storage conditions Shelf life is 6 months for part a and 12 months for part b in a dry place and in original unopened containers at a temperature between 59 and 77°f/(15 and 25° c). Any opened can must be tightly closed under dry nitrogen.