Advantages
Excellent chemical resistance
Good functionality and mechanical properties
Good waterproof performance
Ideal Applications
Technical Data-sheet
| Category |
Measurement |
Value |
Method |
| General properties |
Powder melting point (DSC) |
187 °C/369 °F |
ASTM D3418 |
| Particle size |
60 µm |
ASTM D3451 |
| Bulk density of powder |
0.425 g/cm3 |
ASTM D1895 |
| Density of parts |
1.01 g/cm3 |
ASTM D792 |
| Mechanical properties |
Tensile strength, max load9 , XYTensile strength, max load9 , ZTensile modulus9 , XYTensile modulus9 , ZElongation at break9 , XY
Elongation at break9 , Z
Flexural strength (@ 5%)10 , XY
Flexural strength (@ 5%)10 , Z
Flexural modulus10 , XY
Flexural modulus10 , Z
Izod impact notched (@ 3.2 mm, 23ºC), XYZ |
48 MPa/6960 psi |
ASTM D638 |
| Thermal properties |
Heat deflection temperature (@ 0.45 MPa, 66 psi), XYHeat deflection temperature (@ 0.45 MPa, 66 psi), ZHeat deflection temperature (@ 1.82 MPa, 264 psi), XYHeat deflection temperature (@ 1.82 MPa, 264 psi),Z |
48 MPa/6960 psi |
ASTM D638 |
| 1700 MPa/247 ksi |
ASTM D638 |
| 1800 MPa/261 ksi |
ASTM D638 |
| 20% |
ASTM D638 |
| 15% |
ASTM D638 |
| 65 MPa/9425 psi |
ASTM D790 |
| 70 MPa/10150 psi |
ASTM D790 |
| 1730 MPa/251 ksi |
ASTM D790 |
| 1730 MPa/251 ksi |
ASTM D790 |
| 3.5 kJ/m2 |
ASTM D256 Test Method A |
| 175 ºC/347 ºF |
ASTM D648 Test Method A |
| 175 ºC/347 ºF |
ASTM D648 Test Method A |
| 95 ºC/203 ºF |
ASTM D648 Test Method A |
| 106 ºC/223 ºF |
ASTM D648 Test Method A |
| Recyclability |
Refresh ratio for stable performance |
20% |
|
| Certifications |
USP Class I-VI and US FDA guidance for Intact Skin Surface Devices, RoHS11, EU REACH, PAHs |