- High strength and strong toughness
- Accurate and dimensionally stable
- Excellent temperature resistance
- Good moisture resistance
- Functional model need to be tough
- Conceptual model
- Low volume production models
- Automotive, aerospace, architecture, electronic applications
| Liquid Properties | Optical Properties | ||
| Appearance | Light yellow | Dp | 0.135-0.155 mm |
| Viscosity | 355-455 cps @ 28 ℃ | Ec | 9-12 mJ/cm2 |
| Density | 1.11-1.14g/cm3 @ 25 ℃ | Building layer thickness | 0.05~0.15mm |
| Mechanical Properties | UV Postcure | |
| MEASUREMENT | TEST METHOD | VALUE |
| Hardness , Shore D | ASTM D 2240 | 76-82 |
| Flexural modulus , Mpa | ASTM D 790 | 2,650-2,760 |
| Flexural strength , Mpa | ASTM D 790 | 65- 74 |
| Tensile modulus , MPa | ASTM D 638 | 2,160-2,360 |
| Tensile strength , MPa | ASTM D 638 | 25-30 |
| Elongation at break | ASTM D 638 | 12 -20% |
| Impact strength, notched lzod, J/m | ASTM D 256 | 58 - 70 |
| Heat deflection temperature, ℃ | ASTM D 648 @66PSI | 58-68 |
| Glass transition, Tg | DMA，E’peak | 55-70 |
| Density , g/cm3 | 1.14-1.16 | |
Recommended temperature for processing and storage of the above resin should be 18℃-25℃.