| Liquid Properties | Optical Properties | ||
| Appearance | Brown | Dp | 0.135-0.155 mm |
| Viscosity | 405-505 cps @ 28 ℃ | Ec | 9-12 mJ/cm2 |
| Density | 1.11-1.14g/cm3 @ 25 ℃ | Building layer thickness | 0.1-0.15mm |
| Mechanical Properties | UV Postcure | |
| MEASUREMENT | TEST METHOD | VALUE |
| Hardness , Shore D | ASTM D 2240 | 74-80 |
| Flexural modulus , Mpa | ASTM D 790 | 2,650-2,750 |
| Flexural strength , Mpa | ASTM D 790 | 60- 75 |
| Tensile modulus , MPa | ASTM D 638 | 2,150-2,370 |
| Tensile strength , MPa | ASTM D 638 | 25-30 |
| Elongation at break | ASTM D 638 | 12 -20% |
| Impact strength, notched lzod, J/m | ASTM D 256 | 58 - 70 |
| Heat deflection temperature, ℃ | ASTM D 648 @66PSI | 58-68 |
| Glass transition, Tg | DMA，E”peak | 55-70 |
| Density , g/cm3 | 1.14-1.16 | |
Recommended temperature for processing and storage of the above resin should be 18℃-25℃.